Cryogenic testing of a Brazed Optical Quality SiC Mirror

 Programme:  GSTP  Achieved TRL:  5
 Reference:  G512-007MM  Closure:  2015
 Contractor(s):  AMOS (BE)

 
A 950mm diameter brazed SiC mirror had been manufactured and polished consisting of three individual petals brazed together. It has been shown that an excellent surface form can be achieved in ambient environment despite a different micro-structure of the individual petals. Space application of such mirror will require such quality also at low temperatures, in particular, for science missions.

Objectives
Test whether the different materials combined in this mirror (SiC, brazing agent, CVD SiC cladding layer) will induce distortions of the mirror limiting or preventing application of this mirror technology at low temperatures.

...
Deviation of mirror shape from nominal shape at cryogenic temperatureAccess the image

Achievements
The test was performed down to a temperature of 120K. The surface figure was degraded by 5.8 nm rms with respect to room temperature. This value is in line with FEM predictions and perfectly acceptable for optical telescopes.

Benefits
This test proved that this technology could be employed for optical space telescopes operating in the visible or ultraviolet without significant impact on the imaging performance.

Next steps
A potential follow-up would be the manufacturing and testing of a larger mirror.

Rate this

  • Currently 0 out of 5 Stars.
  • 1
  • 2
  • 3
  • 4
  • 5
Rating: 0/5 (0 votes cast)

Thank you for rating!

You have already rated this page, you can only rate it once!

Your rating has been changed, thanks for rating!

Views

156